TAROMID B 240 Y0
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ThSnGw_TAROMID-B-240-Y0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 6 medium viscosity, UL94 V0 self extinguishing halogen and phosphorus free, low density, very good flow and high tracking resistance. Available: different colours, heat stabilised (H). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 to 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.0 to 1.5 | % | |
| Across Flow | 1.0 to 1.5 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 1.4 to 1.8 | % | ASTM D570, ISO 62 |
| Saturation | 9.0 | % | ASTM D570 |
| Saturation, 23°C | 9.0 | % | ISO 62 |
| Granule Humidity | < 0.10 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3350 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 77.0 | MPa | |
| Break | 62.0 | MPa | |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3100 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- 1 | 115 | MPa | ISO 178 |
| -- 2 | 105 | MPa | ISO 178 |
| Yield | 115 | MPa | ASTM D790 |
| Break | 105 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3(23°C) | 2.7 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 32 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 190 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- 4 | 70.0 | °C | |
| -- 5 | 100 | °C | |
| -- 6 | 100 | °C | |
| -- 7 | 120 | °C | |
| Vicat Softening Temperature | |||
| -- | 204 | °C | ASTM D1525, ISO 306/A50 9 8 |
| -- | 200 | °C | ASTM D1525, ISO 306/B50 10 9 |
| Ball Pressure Test (165°C) | Pass | VDE 0470 | |
| Melting Temperature | 222 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 20 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.970 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 34 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | Yield |
| 2 . | Break |
| 3 . | 6x4x50 mm |
| 4 . | 20000 hrs |
| 5 . | Heat Stabilized, 20000 hrs |
| 6 . | Short Term |
| 7 . | Heat Stabilized, Short Term |
| 8 . | Rate A (50°C/h), Loading 1 (10 N) |
| 9 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Vestolen A 5061R 63363 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| Styrolution PS 158N/L | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| XYLEX™ X8303CL resin | SABIC Innovative Plastics Europe | PC+Polyester | XYLEX™ |
| Lucky Enpla LGF3110R | Lucky Enpla Co LTD | PC+PBT | Lucky Enpla |
| ALTECH® PP-H ECO 4940/500 MR40 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |