Badamid® PA12 H
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Th3P9s_BadamidPA12H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA12 injection moulding grade with 30% glass fibre reinforcement; flame retardant, halogen free |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/1.0 kg) | 9.0 | g/10 min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.70 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ISO 2039-2 | |
| Durometer Hardness (Shore D) | 77 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 1700 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Yield, 23°C) | 47.0 | MPa | ISO 527-2/50 |
| Tensile Strain 3(Yield, 23°C) | 4.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break 4(23°C) | > 200 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C, 4.00 mm) | 1500 | MPa | ISO 178 |
| Flexural Stress 6(23°C, 4.00 mm) | 60.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 45.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 7 | 180 | °C | ISO 3146 |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | DIN 53752 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (1.00 mm) | 1.0E+15 | ohms·cm | IEC 60093 |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | Test Specimen accordng to ISO 3167, Type A |
| 5 . | Test Specimen accordng to ISO 3167, Type A |
| 6 . | Test Specimen accordng to ISO 3167, Type A |
| 7 . | 10 K/Min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide AG7 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Ethylplus 615 MD | Fainplast Compounds S.r.l | MDPE | Ethylplus |
| LNP™ STAT-KON™ KEP33 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ STAT-KON™ |
| Vipel® F737-BCF-00 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| LNP™ THERMOCOMP™ RF0049S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |