NuSil R1-2145
| Category: | Silicone , Silicone |
| Manufacturer: | NuSil Technology |
| Trademark: | NuSil |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Tg3TGa_NuSil-R1-2145.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
The Aircraft Industry has used silicone adhesives and coatings for over five decades. Silicone's ability to maintain its elasticity and low modulus over a broad temperature range provides excellent utility in extreme environments. Recent advances in material technology provide more opportunities for the Aircraft engineer in choosing the best material for an intended application. Examples of NuSil's capabilities in custom silicones for Aircraft are demonstrated in the following sections.
General Purpose: Adhesives and Sealants Comment: Longer Work Time, Young's Modulus 300 psi (2.1 MPa) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 1.0 | ||
| Part B | Mix Ratio by Weight: 1.0 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Cure System | Platinum | ||
| Extrusion Rate | |||
| Part A | 265 | g/min | |
| Part B | 250 | g/min | |
| Operating Temperature | -50 to 200 | °C |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | Grey | ||
| Density | 1.17 | g/cm³ | |
| Curing Time (65°C) | 2.0 | hr | |
| Pot Life | 60 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore A) | 45 | ||
| Lap Shear Strength 1 | 4.31 | MPa | |
| Tensile Modulus | 2.07 | MPa | |
| Tensile Strength | 6.89 | MPa | |
| Tensile Elongation at Break | 400 | % | |
| Tear Strength | 33.3 | kN/m | |
| Electric Strength | 32 | kV/mm |
| Note Message | |
|---|---|
| 1 . | Primed with CF1-135 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® PCR GF 15 K1947 | A. Schulman Europe | PBT+PET | SCHULADUR® |
| TEKAMID™ TA210HI3 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| VALOX™ 357 resin | SABIC Innovative Plastics | PC+PBT | VALOX™ |
| Dynaprene® VE3080A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| LNP™ LUBRICOMP™ OCP34E compound | SABIC Innovative Plastics | PPS, Linear | LNP™ LUBRICOMP™ |