IROGRAN® A 80 H 4698
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Tg0Az2_IROGRAN-A-80-H-4698.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 80 H 4698 is a transparent thermoplastic polyester-polyurethane for injection moulding applications. Additional characteristics of the product are good melt flow and easy demolding also for undercut. PERFORMANCE FEATURES
APPLICATIONS For the production of casual shoe soles, o-rings screens, technical parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.20 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (190°C/21.6 kg) | 50.0 | cm³/10min | |
| Molding Shrinkage - Flow (Injection Molded) | 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore D, Injection Molded | 30 | ASTM D2240 | |
| Shore A, Injection Molded | 81 | ISO 868 | |
| Shore D, Injection Molded | 31 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2 | DIN 53504 | ||
| 100% Strain | 5.90 | MPa | |
| 300% Strain | 15.0 | MPa | |
| Tensile Stress 3(Break) | 47.0 | MPa | DIN 53504 |
| Tensile Elongation 4(Break) | 650 | % | DIN 53504 |
| Tear Strength 5 | 60 | kN/m | ISO 34-1 |
| Compression Set 6 | ASTM D395, ISO 815 | ||
| 23°C, 24 hr | 25 | % | |
| 70°C, 24 hr | 40 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Melting Temperature | 128 to 180 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Hot Air Dryer | 80.0 to 90.0 | °C | |
| Drying Time | |||
| -- | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Rear Temperature | 175 to 190 | °C | |
| Middle Temperature | 175 to 190 | °C | |
| Front Temperature | 175 to 190 | °C | |
| Nozzle Temperature | 180 to 200 | °C | |
| Processing (Melt) Temp | 170 to 195 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 25.0 to 40.0 | °C | |
| Cylinder Zone 1 Temp. | 165 to 190 | °C | |
| Cylinder Zone 2 Temp. | 165 to 190 | °C | |
| Cylinder Zone 3 Temp. | 165 to 190 | °C | |
| Cylinder Zone 4 Temp. | 165 to 190 | °C | |
| Cylinder Zone 5 Temp. | 165 to 190 | °C | |
| Adapter Temperature | 175 to 195 | °C | |
| Die Temperature | 175 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Injection Molded |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ARC ARC5027 | ARC Resin Corporation | Acetal (POM) Copolymer | ARC |
| Generic Nylon 66+Nylon 6I/X - Glass Fiber | Generic | Nylon 66+Nylon 6I/X | Generic |
| ENFLEX S3170A HF | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| HiFill® POM HO GF25 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | HiFill® |
| Vydyne® R535H NT | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |