Quadrant EPP Nylatron® GS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TevDgP_Quadrant-EPP-Nylatron-GS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP Nylatron® GS is a Polyamide 66 (Nylon 66) product. It is available in Europe. Typical application: Engineering/Industrial Parts. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.15 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 3.00 mm | 0.68 | -- | % | |
| Saturation, 23°C | 7.8 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.3 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 3.00 mm 1 | 1.3 | -- | % | |
| 23°C, 3.00 mm 2 | 85.0 | -- | mg | |
| 23°C, 3.00 mm 3 | 46.0 | -- | mg |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Service Temperature - Minimum | -20 | -- | °C |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (M-Scale, 10.0 mm) | 88 | -- | ISO 2039-2 | |
| Ball Indentation Hardness (10.0 mm) | 165 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3500 | 1680 | MPa | ISO 527-2/1B/1 |
| Tensile Stress (Yield) | 92.0 | 55.0 | MPa | ISO 527-2/1B/20 |
| Tensile Strain (Break) | 20 | > 50 | % | ISO 527-2/1B/20 |
| Tensile Creep Modulus (1000 hr) | 21.0 | 9.00 | MPa | ISO 899-1 |
| Compressive Stress | ISO 604/1 | |||
| 5% Strain | 92.0 | -- | MPa | |
| 2% Strain | 49.0 | -- | MPa | |
| 1% Strain | 25.0 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact Strength | 4.0 | 9.0 | kJ/m² | ISO 180/2A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 85.0 | -- | °C | ISO 75-2/A |
| Continuous Use Temperature | ||||
| -- 4 | 80.0 | -- | °C | |
| -- 5 | 95.0 | -- | °C | |
| -- 6 | 180 | -- | °C | |
| Melting Temperature (DSC) | 255 | -- | °C | |
| CLTE - Flow | ||||
| 23 to 60°C | 8.0E-5 | -- | cm/cm/°C | |
| 23 to 100°C | 9.0E-5 | -- | cm/cm/°C | |
| Thermal Conductivity (23°C) | 0.29 | -- | W/m/K |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | > 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm, in Oil) | 26 | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.80 | 7.40 | ||
| 1 MHz | 3.30 | 3.80 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.013 | 0.13 | ||
| 1 MHz | 0.020 | 0.060 | ||
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 3.00 mm | HB | -- | ||
| 6.00 mm | HB | -- | ||
| Oxygen Index | 26 | -- | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 96 hrs |
| 2 . | Weight, 96 hrs |
| 3 . | Weight, 24 hrs |
| 4 . | 20000 hrs |
| 5 . | 5000 hrs |
| 6 . | Short periods |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propilven J-901 | Propilven, S.A. | PP Homopolymer | Propilven |
| Monprene® CP-28126 | Teknor Apex Company | TPE | Monprene® |
| Nucrel® 0910 | DuPont Packaging & Industrial Polymers | EMAA | Nucrel® |
| Karina GRAY PVC COMPOUND -E 801-18/396-A-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Zetpol® 2010H | Zeon Corporation | NBR | Zetpol® |