Durethan® BM 240 H3.0 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TeWhOn_DurethanBM240H30000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 40 % mineral, injection molding, heat-aging stabilized, low tendency to warp, isotopic properties |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.44 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.85 | -- | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.25 | -- | % | ISO 294-4 |
| Flow direction : 280°C, 2.00mm 3 | 0.85 | -- | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.25 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C | 5630 | 2140 | MPa | ASTM D638 |
| 23°C | 5700 | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Fracture, 23°C | 82.7 | 53.1 | MPa | ASTM D638 |
| Fracture, 23°C | 85.0 | 55.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | ||||
| Fracture, 23°C | 10 | 40 | % | ASTM D638 |
| Fracture, 23°C | 5.5 | 40 | % | ISO 527-2/5 |
| Flexural Modulus | ||||
| 23°C | 5600 | 2000 | MPa | ASTM D790 |
| 23°C 5 | 5500 | 2000 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 23°C | 150 | 64.8 | MPa | ASTM D790 |
| 3.5% strain 6 | 130 | 60.0 | MPa | ISO 178/A |
| 23°C 7 | 140 | 65.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 8(23°C) | 5.5 | 8.0 | % |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 9 | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 14-060, MD40 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Film Puncture Energy | ISO 6603-2 | |||
| -- 10 | 3.00 | -- | J | ISO 6603-2 |
| -- 11 | 20.0 | 65.0 | J | ISO 6603-2 |
| Film Puncture Force | ISO 6603-2 | |||
| -- 12 | 728 | -- | N | ISO 6603-2 |
| -- 13 | 3030 | -- | N | ISO 6603-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 130 | 80 | kJ/m² | ISO 179/1eU |
| 23°C | 150 kJ/m² | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 100 | 85 | kJ/m² | ISO 180/1U |
| 23°C | 130 kJ/m² | No Break | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 185 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 85.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 200 | -- | °C | ISO 306/B120 |
| Melting Temperature 14 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 6.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 7.0E+15 | -- | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 4.0E+15 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 36 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 4.50 | -- | IEC 60250 | |
| 23°C, 1 MHz | 4.00 | -- | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 23°C, 100 Hz | 0.026 | -- | IEC 60250 | |
| 23°C, 1 MHz | 0.024 | -- | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 15 | 27 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | Pull Rate: 2 mm/min; 50% RH |
| 9 . | US-FMVSS302 |
| 10 . | -30°C |
| 11 . | 23°C |
| 12 . | -30°C |
| 13 . | 23°C |
| 14 . | 10°C/min |
| 15 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 199 X 124797 A | RTP Company | PP, Unspecified | RTP |
| Telcar® TL-2560A | Teknor Apex Company | TPE | Telcar® |
| NEFTEKHIM PP 8332M (EPC40R) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| ADDILENE J 510 | ADDIPLAST | PP Copolymer | ADDILENE |
| ASTALAC™ ABS BSMG | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |