Pyramid™ PEEK CC100
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Polymics, Ltd. |
| Trademark: | Pyramid™ PEEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TeKur1_Pyramid-PEEK-CC100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PEEK with 60% Chopped Carbon Fabric/Tape |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 110 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 36000 | MPa | ASTM D638 |
| Tensile Strength (Break) | 310 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 34000 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 330 | MPa | ASTM D790 |
| Compressive Modulus | 25000 | MPa | ASTM D695 |
| Compressive Strength | 275 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (0.318 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 300 | °C | ASTM D648 |
| Glass Transition Temperature | 143 | °C | ASTM E1356 |
| Melting Temperature | 340 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+2 | ohms | ASTM D257 |
| Volume Resistivity | < 1.0E+2 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCLAIR® 2909 | NOVA Chemicals | HDPE | SCLAIR® |
| TOTAL Polypropylene PPH 3827WZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| NILAMID® A3 TM2 | Nilit Plastics | Nylon 66 | NILAMID® |
| LUVOCOM® 1105-0779/WT | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Plexiglas® MI7T | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |