DOW™ Electrical & Telecommunications DFDK-6010 BK

Category:	PE, Unspecified , Carbon Black Masterbatch for Jacket Applications
Manufacturer:	The Dow Chemical Company
Trademark:	DOW™ Electrical & Telecommunications
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	TeCcXB_DOW-Electrical-Telecommunications-DFDK-6010-BK.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
DOW™ Electrical & Telecommunications DFDK-6010 BK is a carbon black filled masterbatch and contains an ageing stabilizer. It is specifically designed to be compatible with Dow Polyethylene Resins for use as black telecom, power and fiber optic cables. To achieve 2.6 % carbon black in the finished jacket, DOW™ Electrical & Telecommunications DFDK-6010 BK should be incorporated at a level of 6.2 %. With the recommended carbon black content DOW™ Electrical & Telecommunications DFDK-6010 BK provides excellent UV protection for telecom, power and fiber optic cables. Processing: DFDK-6010 BK carbon black masterbatch and the selected Dow Polyethylene Resin should be introduced to the extruder hopper uniformly in the correct ratio to ensure a consistent 2.6% carbon black throughout the final product. Use melt extrusion temperatures appropriate for the chosen base resin.

Message

DOW™ Electrical & Telecommunications DFDK-6010 BK is a carbon black filled masterbatch and contains an ageing stabilizer. It is specifically designed to be compatible with Dow Polyethylene Resins for use as black telecom, power and fiber optic cables. To achieve 2.6 % carbon black in the finished jacket, DOW™ Electrical & Telecommunications DFDK-6010 BK should be incorporated at a level of 6.2 %.
With the recommended carbon black content DOW™ Electrical & Telecommunications DFDK-6010 BK provides excellent UV protection for telecom, power and fiber optic cables.

Processing:
DFDK-6010 BK carbon black masterbatch and the selected Dow Polyethylene Resin should be introduced to the extruder hopper uniformly in the correct ratio to ensure a consistent 2.6% carbon black throughout the final product. Use melt extrusion temperatures appropriate for the chosen base resin.

General Information
Uses	Cable Jacketing Masterbatch Wire & Cable Applications
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Apparent Density	0.66	g/cm³	ISO 60
Melt Mass-Flow Rate (MFR) (190°C/21.6 kg)	32	g/10 min	ISO 1133
Carbon Black Content	42	%	IEC 60811-4-1
Moisture	< 2.0	%	DIN 53715

Resin Grade	Manufacturer	Category	Trademark
RTP 200D L	RTP Company	Nylon 612	RTP
SABIC® HDPE M864SE	Saudi Basic Industries Corporation (SABIC)	HDPE	SABIC® HDPE
Medalist® MD-12350	Teknor Apex Company	TPE	Medalist®
Cheng Yu T882GV1	Cheng Yu Plastic Company Limited	PBT	Cheng Yu
Hyosung Polyketone M340A	Hyosung Corporation	PK-Aliphatic	Hyosung Polyketone