Celanex® 2300 GV3/30
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TctyFf_Celanex-2300-GV3-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Chemical abbreviation according to ISO 1043-1: PBT Moulding compound ISO 7792- PBT, MGHR, 08-040N, GB30 Polybutylene terephthalate, low warpage, 30 % glass beads. Flammability UL 94 HB minimum thickness 0.82 mm. Recognition by Underwriters Laboratories, USA (UL) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Multi-Point Data |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 10.0 | cm³/10min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 50.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/1A/5 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 3600 | MPa | ISO 899-1 |
| 1000 hr | 2500 | MPa | ISO 899-1 |
| Flexural Stress (23°C) | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.3 | kJ/m² | ISO 179/1eA |
| 23°C | 3.3 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 23 | kJ/m² | ISO 179/1eU |
| 23°C | 22 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 190 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 195 | °C | ISO 306/B50 |
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 28 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.60 | IEC 60250 | |
| 1 MHz | 4.40 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 9.0E-3 | IEC 60250 | |
| 1 MHz | 0.012 | IEC 60250 | |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.820 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| Oxygen Index | 22 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 250 - 260 | °C | |
| Middle Temperature | 250 - 260 | °C | |
| Front Temperature | 255 - 265 | °C | |
| Nozzle Temperature | 260 - 270 | °C | |
| Processing (Melt) Temp | 260 - 270 | °C | |
| Mold Temperature | 75.0 - 100 | °C | |
| Injection Pressure | 60.0 - 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Back Pressure | 1.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 260 to 270°CZone 4 Temperature: 255 to 265°CFeed Temperature: 190 to 200°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BUM 30 | Arkema | Nylon 11 | Rilsan® |
| Shandong PA1212 G121B01 | Shandong Guangyin New Materials Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| Adell Polyamide AT-33 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Aplax P2313CN | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| EPLAMID 66 GFS 40 HS NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |