Anjacom® 055/80-GF20 Black 91210
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Almaak International GmbH |
| Trademark: | Anjacom® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TcgTTV_Anjacom-055-80-GF20-Black-91210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Anjacom® 055/80-GF20 Black 91210 is a Polycarbonate + ABS (PC+ABS) material filled with 20% glass fiber. It is available in Europe for injection molding. Primary attribute of Anjacom® 055/80-GF20 Black 91210: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.25 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.20 to 0.50 | % | |
| Flow | 0.30 to 0.60 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.60 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 105 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 8.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 34 | kJ/m² | |
| 23°C | 35 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 133 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 122 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 135 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AT0110GN | Ginar Technology Co., LTD. | Nylon 66 | Mapex |
| RTP 3205 | RTP Company | ETFE | RTP |
| SITRAROY 2015 / C94150 | SITRAPLAS GmbH | ASA+PC | SITRAROY |
| DIC.PPS Z-200-E5 | DIC Corporation | PPS | DIC.PPS |
| Tribocomp® PA66 LGF30 PTFE18 N6 | Solvay Specialty Polymers | Nylon 66 | Tribocomp® |