DILAMID® 6 FVT 30 NAT A
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Dilaplast S.p.A. |
| Trademark: | DILAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TcWdNA_DILAMID-6-FVT-30-NAT-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DILAMID® 6 FVT 30 NAT A is a Polyamide 6 (Nylon 6) material filled with 30% glass fiber. It is available in Europe for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.30 to 0.35 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 6.50 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 6.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 200 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 2.0 to 8.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 240 to 280 | °C | |
| Middle Temperature | 250 to 290 | °C | |
| Front Temperature | 260 to 300 | °C | |
| Nozzle Temperature | 255 to 295 | °C | |
| Processing (Melt) Temp | 260 to 300 | °C | |
| Mold Temperature | 70.0 to 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® 3019 HS | PolyPacific Pty. Ltd. | PP, Unspecified | Retpol® |
| XYRON™ AG512 | Asahi Kasei Chemicals Corporation | Nylon+PPE | XYRON™ |
| CMET TSR-883 | CMET Inc. | Epoxy | CMET |
| Fiberfil® PP-62/CC/20/UV | Fiberfil® Engineered Plastics Inc. | PP Copolymer | Fiberfil® |
| LNP™ THERMOCOMP™ PX01658 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |