Zytel® FG42A NC010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TbAGCD_Zytel-FG42A-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced High Viscosity Polyamide 66 with Developed for Food Contact Applications |
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.4 | -- | % | |
| Flow | 1.4 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 8.5 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.6 | -- | % | |
| Viscosity Number | 280 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3100 | 1300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 83.0 | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.4 | 27 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2800 | 1070 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | 4.0 | kJ/m² | |
| 23°C | 6.0 | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 7.0 | 6.0 | kJ/m² | |
| 23°C | 6.0 | 23 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 70.0 | -- | °C | ISO 11357-2 |
| Vicat Softening Temperature | 244 | -- | °C | ISO 306/B50 |
| Melting Temperature 2 | 262 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.0E-4 | -- | cm/cm/°C | |
| Transverse | 1.0E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 31 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.30 | 10.0 | ||
| 1 MHz | 3.60 | 4.20 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.015 | 0.20 | ||
| 1 MHz | 0.015 | 0.075 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 3.00 mm | V-2 | -- | ||
| 1.50 mm | HB | -- | ||
| Oxygen Index | 28 | -- | % | ISO 4589-2 |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 1.01 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2790 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.16 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CALP 3850G | Lion Idemitsu Composites Co., Ltd. | ABS | CALP |
| Formolene® L42009E2 | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| EPO-TEK® EK1000-MP | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Hostacom EKC 430N | LyondellBasell Industries | PP Copolymer | Hostacom |
| Plexiglas® Hi-Gloss NTA-3 | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |