Marlex® HMN TR-935G

Category:	MDPE , Medium Density Polyethylene
Manufacturer:	Chevron Phillips Chemical Company LLC
Trademark:	Marlex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	TapN9i_MarlexHMNTR935G.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

These hexene copolymers are tailored for rotational molding applications that require:

Wide process windows

Excellent impact strength

Good flow

Excellent ESCR

Typical applications for HMN TR-935 and HMN TR-935G include items such as:

Recreational and agricultural equipment

Toys and carts

These resins are available in:

Pellet form - HMN TR-935

35 US mesh powder - HMN TR-935G

These resins meet these specifications:

ASTM D4976 - PE 223

FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per 21 CFR 176.170(c) Table 2. Single use articles contacting food types I, II, IV-B, VI-A, VI-B, VII-B, and VIII. Repeated use articles contacting all food types defined in 21 CFR 176.170(c) Table 1.

NSF / ANSI Standard 61 for potable water (CLD 23)

NSF / ANSI Standard 51 for any food contact (MTU 100°C)

UL94HB yellow card per UL file E349283

UL746C (f1) yellow card per UL file E349283

FMVSS.302 burn test

AS/NZS 4020:2005 (contact with drinking water)

Long term UV stabilization - ASTM 2565 (Cycle 1): Greater than UV-16

General Information
Additive	UV stabilizer
Features	High ESCR (Stress Cracking Resistance) hexene comonomer Impact resistance, good Good UV resistance Good liquidity
Uses	Agricultural application Sporting goods Toys
Agency Ratings	AS/NZS 4020:2005 ASTM D 2565 ASTM D 4976-PE223 FDA 21 CFR 177.1520(c) 3.2a 2 NSF 51 NSF 61
UL File Number	E54700
Forms	Powder
Processing Method	rotomolding

Physical	Nominal Value	Unit	Test Method
Density	0.939	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	6.0	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance			ASTM D1693A
10% Igepal, molded, F50	130	hr	ASTM D1693A
100% Igepal, molded, F50	> 1000	hr	ASTM D1693A
Outdoor Suitability	f1		UL 746C

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, Compression Molded)	59		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield, 3.17 mm, Rotational Molded)	17.0	MPa	ASTM D638
Tensile Elongation ²(Break, 3.17 mm, Rotational Molded)	750	%	ASTM D638
Flexural Modulus ³			ASTM D790
2% positive cut : mm, rotational molding	620	MPa	ASTM D790
Tangent : mm, rotational molding	760	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
ARM Impact
-40°C, 3.20 mm	102	J
-40°C, 6.35 mm	237	J

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, unannealed, 3.17mm, rotational molding	58.0	°C	ASTM D648
1.8 MPa, unannealed, 3.17mm, rotational molding	41.0	°C	ASTM D648
Brittleness Temperature	-75.0	°C	ASTM D746A
Vicat Softening Temperature	110	°C	ASTM D1525 ⁴
Peak Melting Temperature	128	°C	ASTM D3418
Peak Crystallization Temperature (DSC)	112	°C	ASTM D3418

Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94

Note Message
1 .	Type 4, 51mm/min
2 .	Type 4, 51mm/min
3 .	13 mm/min
4 .	速率 A (50°C/h), 压力1 (10N)

Resin Grade	Manufacturer	Category	Trademark
Shandong PA6 A1RG6301	Shandong Dongchen Engineering Plastics Co., Ltd.	Nylon 6	Shandong PA6
Fainplast PVC GK 88	Fainplast Compounds S.r.l	PVC, Unspecified	Fainplast PVC
Hylon® N1025THLUV2	Ravago Manufacturing Americas, LLC	Nylon 66	Hylon®
ICORENE® 7620 Fuel Lock	ICO Polymers EMEA, A Division of A. Schulman	Nylon 6	ICORENE®
NORYL™ SE100X resin	SABIC Innovative Plastics	PPE+PS	NORYL™