FINGERPRINT™ DFDA-7510 NT
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | FINGERPRINT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ta7P5d_FINGERPRINT-DFDA-7510-NT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FINGERPRINT™DFDA-7510 NT linear low density polyethylene resin was prepared by UNIPOL™Processing technology. It is used in the processing of micro-irrigation pipes, durable hoses and pipe fittings, profile extrusion and injection molding fittings. this product can also be used as a blending component for the modification of high pressure, ultra-low density, linear low density or high density polyethylene resin to improve its physical properties. Outdoor applications need to add UV stabilizers to maintain excellent performance under long-term UV exposure. Main features:
slip agent content: none opening agent content: none industry standard
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.60 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 44 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance 1(F0) | > 500 | hr | ASTM D1693A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 2(Shore D) | 44 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 3 | ASTM D638 | ||
| Yield | 11.0 | MPa | ASTM D638 |
| Fracture | 15.5 | MPa | ASTM D638 |
| Tensile Elongation 4(Break) | 800 | % | ASTM D638 |
| Flexural Modulus 5 | 310 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 6 | < -100 | °C | ASTM D746A |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 196 - 221 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆类型：所有标准的商用挤出设备。 熔体温度范围：385 - 430 °F (196 - 221 °C) |
| Note Message | |
|---|---|
| 1 . | Prepare the compression molding fitting as per D3350; ASTM D 1928 procedure C. Attributes will vary with molding conditions and aging time. |
| 2 . | Prepare the compression molded fitting according to ASTM D 1928 procedure C. Attributes will vary with molding conditions and aging time. |
| 3 . | Prepare the compression molded fitting according to ASTM D 1928 procedure C. Attributes will vary with molding conditions and aging time. |
| 4 . | Prepare the compression molded fitting according to ASTM D 1928 procedure C. Attributes will vary with molding conditions and aging time. |
| 5 . | Prepare the compression molded fitting according to ASTM D 1928 procedure C. Attributes will vary with molding conditions and aging time. |
| 6 . | Prepare the compression molded fitting according to ASTM D 1928 procedure C. Attributes will vary with molding conditions and aging time. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide RF006K | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Fainplast PVC GS 74 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| ESPREE™ NY613GF | SABIC Innovative Plastics | Nylon 6 | ESPREE™ |
| LEXAN™ 920A resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Karina WHITE PVC COMPOUND BT-0002/17 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |