Ultramid® Structure A3WG8 LFX BK23215
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TZD4tg_UltramidStructureA3WG8LFXBK23215.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid Structure A3WG8 LFX BK23215 is a 40% long glass-fiber reinforced and heat aging resistant injection molding grade designed for applications requiring excellent strength and stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.47 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.66 | -- | % | ISO 294-4 |
| Flow | 0.45 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 13500 | 10200 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 240 | 169 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.4 | 2.4 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 12400 | 9300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 360 | 268 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 22 | 20 | kJ/m² | ISO 179 |
| 23°C | 21 | 21 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 68 | 63 | kJ/m² | ISO 179 |
| 23°C | 82 | 82 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 290 - 310 | °C | |
| Mold Temperature | 80 - 100 | °C | |
| Injection Pressure | 3.50 - 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ ATC-000/000 AS Natural | PolyOne Corporation | Acetal (POM) Copolymer | Stat-Tech™ |
| Verolloy A5626 | PlastxWorld Inc. | ABS+Nylon | Verolloy |
| AKROMID® A3 GF 35 1 natural (2393) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| AXELERON™ CS O-3364 NT CPD | The Dow Chemical Company | HDPE | AXELERON™ |
| Karina IVORY PVC COMPOUND KAPU 5535/1-Y(***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |