NORYL™ HNA055 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TYGpEo_NORYL-HNA055-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| >PPE+PS-HI< Autoclavable engineering thermoplastic. Biocompatible per ISO10993 (color dependent). |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 6.2 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 5.70 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 to 0.80 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.23 | % | |
| Equilibrium, 23°C, 50% RH | 0.060 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3250 | MPa | ASTM D638 |
| -- | 2410 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 67.9 | MPa | ASTM D638 |
| Yield | 61.8 | MPa | ISO 527-2/50 |
| Break 3 | 55.5 | MPa | ASTM D638 |
| Break | 57.6 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.8 | % | ASTM D638 |
| Yield | 3.8 | % | ISO 527-2/50 |
| Break 5 | 16 | % | ASTM D638 |
| Break | 13 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2540 | MPa | ASTM D790 |
| -- 7 | 2490 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 107 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 101 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 27 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 140 | J/m | ASTM D256 |
| 23°C | 290 | J/m | ASTM D256 |
| -30°C 10 | 15 | kJ/m² | ISO 180/1A |
| 23°C 11 | 25 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 54.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 147 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 148 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 168 | °C | ASTM D1525, ISO 306/B50 10 13 |
| -- | 169 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 9.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 260 to 304 | °C | |
| Middle Temperature | 271 to 310 | °C | |
| Front Temperature | 282 to 316 | °C | |
| Nozzle Temperature | 293 to 316 | °C | |
| Processing (Melt) Temp | 293 to 316 | °C | |
| Mold Temperature | 76.7 to 104 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pushtrusion™ D-GMT LGF34-PP NAT | PlastiComp, Inc. | PP, Unspecified | Pushtrusion™ |
| SEPAZ™ C130HS | Mando Advanced Materials Co., Ltd. | LCP | SEPAZ™ |
| Abstron IM21G | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Arak LLDPE HD5620EA | Shazand (Arak) Petrochemical Corporation | HDPE | Arak LLDPE |
| Optix® CA-927 HF CLEAR | Plaskolite West, Inc. | Acrylic (PMMA) | Optix® |