Next Nylon 6 Prime Series NXIM-01NC
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 6 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TXgdcK_Next-Nylon-6-Prime-Series-NXIM-01NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA6 Un Filled Impact modified Natural Compound Product Applications Generally recommended for automotive component and industrial parts. cold weather and high impact supports gear Benefits Excellent Mechanical properties with good impact strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.10 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 1.2 | -- | % | |
| Across Flow | 1.4 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 2.1 | -- | % | |
| Saturation 1 | 8.2 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 65.0 | 40.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | 60 | % | ASTM D638 |
| Flexural Modulus | 2600 | -- | MPa | ASTM D790 |
| Flexural Strength | 105 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -30°C | 88 | -- | J/m | |
| 23°C | 110 J/m | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 145 | -- | °C | |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | |
| Melting Temperature | 220 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 25 | 20 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Mold Temperature | 65.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stylac™ IX600 | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| THERMOLAST® K TC6GPN (Series: GP/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Multilon® DN-3720F | TEIJIN LIMITED | PC+ABS | Multilon® |
| Nylene® 5133 HS | Custom Resins Group | Nylon 66 | Nylene® |
| ALCOM® PA66 910/1.3 CF5 GF25 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |