HiFill FR® PA6 GF33 FR-NR
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill FR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TX5mNF_HiFill-FR-PA6-GF33-FR-NR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill FR® PA6 GF33 FR-NR is a Polyamide 66 (Nylon 66) product filled with glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.58 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 827 | MPa | ISO 527-2 |
| Tensile Strength (Break) | 134 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638 |
| Flexural Modulus | 483 | MPa | ASTM D790 |
| Flexural Strength | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 216 | °C | |
| 1.8 MPa, Unannealed | 216 | °C | |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | > 6.0 | hr | |
| Rear Temperature | 254 to 277 | °C | |
| Middle Temperature | 254 to 277 | °C | |
| Front Temperature | 254 to 277 | °C | |
| Processing (Melt) Temp | 249 to 271 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Task® 11 | Smooth-On, Inc | PUR, Unspecified | Task® |
| Xuchuan XCS-3055B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Evoprene™ GC 5684 | AlphaGary | SEBS | Evoprene™ GC |
| Karina WHITE PVC COMPOUND 846-10/114-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SABIC® LLDPE 218BE | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |