ISPLEN® PM284 AV
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ISPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TWZm72_ISPLEN-PM284-AV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene copolymer, 20% mineral fillers reinforced and high processability. ISPLEN® PM284 AV shows high stiffness and good impact strength. It gives good aesthetic properties and high gloss surface. This product is UV stabilised. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 0.63 to 0.75 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 24.0 | MPa | |
| Break | 19.5 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.0 | % | |
| Break | 22 | % | |
| Flexural Modulus | 2350 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 1.8 | kJ/m² | |
| 0°C | 2.0 | kJ/m² | |
| 23°C | 3.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 25 | kJ/m² | |
| 0°C | 30 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 4.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 59.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 148 | °C | ISO 306/A120 |
| -- | 76.0 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 150x100x3mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TIPPLEN® R 780 | MOL Petrochemicals Co. Ltd. | PP Random Copolymer | TIPPLEN® |
| APEX® 78-A447H-18 | Teknor Apex Company | PVC, Flexible | APEX® |
| TOTAL Polyethylene Lumicene® M 4043 UV (US) | TOTAL Refining & Chemicals | mMDPE | TOTAL Polyethylene |
| LinGen FR180 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PPE | LinGen |
| LEXAN™ 103 resin | SABIC Innovative Plastics | PC | LEXAN™ |