SABIC® LDPE 1815AN00
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TWRBAn_SABIC-LDPE-1815AN00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® LDPE 1815AN00 is an additive free autoclave grade with a specific broad molecular weight distribution and a low viscosity. The material can be processed at high speeds, at low coating weights and for coextrusion with e.g. a bonding polymer, where fhin layers are required. Due to it's low zero viscosity it can be used for coatings with non wovens and textiles. Moreover it permits a low welding temperature (< 100 °C). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance 1(60°C, 2.00mm, molded) | 2.00 | hr | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/200 | ||
| Yield, 1.60mm, molded | 8.00 | MPa | ISO 527-2/200 |
| Fracture, 1.60mm, molded | 14.0 | MPa | ISO 527-2/200 |
| Tensile Strain (fracture, 1.60mm, molded) | 490 | % | ISO 527-2/200 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm | 8.00 | MPa | ISO 527-3 |
| TD : Yield, 25 µm | 8.00 | MPa | ISO 527-3 |
| MD : 25 µm | 11.0 | MPa | ISO 527-3 |
| TD : 25 µm | 9.00 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm | 350 | % | ISO 527-3 |
| TD : Break, 25 µm | 300 | % | ISO 527-3 |
| Water Vapor Transmission Rate (38°C, 100% RH, 25 µm) | 22 | g/m²/24 hr | Internal method |
| Oxygen Permeability (23°C, 25.0 µm) 2 | 0.90 | cm³/cm²/bar/24 hr | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Enthalpy Change | 97.0 | J/g | DIN 53765 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Crack Resistance (25.0 µm) 3 | 3000 | cycles/10 holes | Internal method |
| Tear Strength | ISO 6383-2 | ||
| MD : 25.0 µm | 9.0 | kN/m | ISO 6383-2 |
| TD : 25.0 µm | 7.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 86.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 105 | °C | DIN 53765 |
| Note Message | |
|---|---|
| 1 . | 2 MPa |
| 2 . | 0% RH |
| 3 . | cycles/10 holes |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RC Plastics RCPA66 | RC Plastics, Inc. (Div. of LNP Engineering Plastics) | Nylon 66 | RC Plastics |
| Starex BF-0677HF | SAMSUNG SDI CO., LTD. | MABS | Starex |
| Zhongfa PET G20S | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PET | Zhongfa |
| Hypro® PPH-CC40 NATURAL | Entec Polymers | PP Homopolymer | Hypro® |
| Laprene® 830000863 | SO.F.TER. SPA | SEBS | Laprene® |