NILAMID® B2 HH GF60
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nilit Plastics |
| Trademark: | NILAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TVRPVs_NILAMID-B2-HH-GF60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NILAMID® B2 HH GF60 is a Polyamide 6 (Nylon 6) compound, 60% glass fiber reinforced, high heat stabilized. This high stiffness and glossy finish compound is intended for injection molding. NILAMID® B2 HH GF60 is primarily designed for the Automotive industry. It is also suitable for Electrical and Electronic or Industrial & Consumer applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.65 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 0.35 | % | |
| Flow : 23°C | 0.20 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.50 | % | |
| Saturation, 23°C | 4.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 18000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 235 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 23°C | 75 | kJ/m² | |
| 30°C | 60 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 15 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 222 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 130 | °C | IEC 60216 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | ||
| 165°C | Pass |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 2 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 22 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 650 | °C | |
| 3.20 mm | 650 | °C | |
| Oxygen Index | 25 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 20000 hr |
| 2 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| API PS 410 | American Polymers, Inc. | PS (GPPS) | API PS |
| CERTENE™ LDF-0522P | Muehlstein | LDPE | CERTENE™ |
| Generic Phenolic - Glass Fiber | Generic | Phenolic | Generic |
| Geon™ Vinyl Rigid Molding M5015 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| LUVOCOM® 1/GF/40/TF/13 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |