Aplax P2515GN
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ginar Technology Co., LTD. |
| Trademark: | Aplax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TVLgdC_Aplax-P2515GN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aplax P2515GN is a high gloss PP with 25 % BaSO4 filler product for injection moulding in natural colour |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (1.60 mm) | 1.0 - 1.3 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 33.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 60 | % | ISO 527-2 |
| Flexural Modulus | 2760 | MPa | ISO 178 |
| Flexural Stress | 68.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 135 | °C | ISO 75-2/B |
| Melting Temperature | > 165 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Additional Information |
|---|
| Notched Izod Impact Strength, ISO 180/1, notch 0.25in: 43 kg cm/cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 - 220 | °C | |
| Middle Temperature | 170 - 220 | °C | |
| Front Temperature | 170 - 220 | °C | |
| Nozzle Temperature | 210 - 220 | °C | |
| Mold Temperature | 30.0 - 100 | °C | |
| Injection Pressure | 50.0 - 120 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 30.0 - 80.0 | MPa | |
| Back Pressure | 0.00 - 0.300 | MPa | |
| Screw Speed | 60 - 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Baoding 76E95 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyether | Baoding |
| Aropol™ MR 642 | Ashland Performance Materials | Polyester, TS | Aropol™ |
| Daelim Po1y® 5502-03LD | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| PLUSTEK RA303G50 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| Europrene Latice® 1142 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |