WONDERLOY® PC-345
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | WONDERLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TVDcqC_WONDERLOY-PC-345.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WONDERLOY® PC-345 is a Polycarbonate + ABS (PC+ABS) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Spiral Flow | 11.9 | cm | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 49.0 | MPa | ASTM D638 |
| Yield | 45.0 | MPa | ISO 527-2/50 |
| Break | 39.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break, 23°C | 85 | % | ASTM D638 |
| Break | 80 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 23°C | 2260 | MPa | ASTM D790 |
| -- 1 | 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 73.5 | MPa | ASTM D790 |
| -- 2 | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 3.18 mm | 480 | J/m | ASTM D256 |
| -- | 39 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed 3 | 95.0 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa, Annealed | 106 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 125 | °C | ASTM D1525, ISO 306/A50 7 4 |
| -- | 110 | °C | ISO 306/B50 |
| CLTE - Flow (40 to 100°C) | 6.0E-5 to 8.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 200 to 230 | °C | |
| Middle Temperature | 230 to 270 | °C | |
| Front Temperature | 220 to 260 | °C | |
| Mold Temperature | 50.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/hr |
| 4 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SCT-150 | SHIN-A T&C | Epoxy | SHIN-A |
| Unichem 8011A-02 | Colorite Polymers | PVC, Unspecified | Unichem |
| EPO-TEK® OE121 Black | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| LNP™ LUBRILOY™ D2000P compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |
| Sylvin 9077-85 Grey 9334 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |