Pibiter® N100 NAT001
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Pibiter® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TV6YWT_Pibiter-N100-NAT001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viscosity PBT unreinforced grade |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 1.7 | % | Internal Method |
| Water Absorption | |||
| 23°C, 24 hr | 0.050 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.35 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2550 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 52.0 | MPa | |
| Break | 34.0 | MPa | |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 2500 | MPa | ASTM D790 |
| Flexural Strength | 87.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 55.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 175 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.20 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 2.0E-3 | ASTM D150 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 235 | °C | |
| Middle Temperature | 250 | °C | |
| Front Temperature | 260 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® FPP 30 T SHH REC | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| SILVER® SA-5324 | Guangdong Silver Age Sci & Tech. Co., Ltd | Polyolefin, Unspecified | SILVER® |
| SUPREME PP SPEXP64 | Supreme Petrochem Ltd. | PP, Unspecified | SUPREME PP |
| LUVOCOM® 1104-7471 | Lehmann & Voss & Co. | PEK | LUVOCOM® |
| Sylvin 6920X08 Grey 9631 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |