ACRYLITE® H12

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Cyro LLC
Trademark:	ACRYLITE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	TV0S08_ACRYLITE-H12.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

ACRYLITE® H12 acrylic polymer is an amorphous thermoplastic molding and extrusion compound based on polymethyl methacrylate (PMMA).

Typical properties of ACRYLITE® acrylic polymers are:

excellent weather resistance

high light transmission

high mechanical strength

high surface hardness and mar resistance

good melt flow rate

versatile colorability due to crystal clarity

The special properties of ACRYLITE H12 polymer are:

medium heat resistance

medium melt flow rate

UV light transmitting

Low levels of lubricant

Application:
Used for injection molding and extrusion of optical and technical parts.

General Information
Additive	Lubricant
Features	Amorphous Good Colorability Good Flow Good Weather Resistance High Clarity High Hardness High Strength Lubricated Medium Heat Resistance Scratch Resistant
Uses	Decorative Displays Electrical/Electronic Applications Engineering Parts Lenses Lighting Applications Medical/Healthcare Applications Optical Applications Piping Profiles Rods Tubing
Agency Ratings	EC 1907/2006 (REACH)
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Extrusion Injection Molding Pipe Extrusion Profile Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.19	g/cm³	ASTM D792
Apparent Density	0.66	g/cm³	ASTM D1895
Melt Mass-Flow Rate (MFR) (230°C/3.8 kg)	7.0	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.40 to 0.60	%	ASTM D955
Water Absorption (Equilibrium)	< 0.30	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	94		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3240	MPa	ASTM D638
Tensile Strength	65.5	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	4.0 to 6.0	%
Break	4.0 to 6.0	%
Flexural Modulus	3380	MPa	ASTM D790
Flexural Strength	117	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 6.35 mm)	19	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm)	93.9	°C	ASTM D648
Vicat Softening Temperature	105	°C	ASTM D1525
CLTE - Flow (0 to 156°C)	7.2E-5	cm/cm/°C	ASTM D696

Optical	Nominal Value	Unit	Test Method
Transmittance (3200 µm)	92.0	%	ASTM D1003
Haze (3200 µm)	< 1.0	%	ASTM D1003
Yellowness Index (3.20 mm)	< 1.0	YI	ASTM D1925

Resin Grade	Manufacturer	Category	Trademark
SABIC® PPcompound 17T1022	Saudi Basic Industries Corporation (SABIC)	PP, Unspecified	SABIC® PPcompound
ALTECH® PA6 A 1000/677	ALBIS PLASTIC GmbH	Nylon 6	ALTECH® PA6
Celstran® PP-GF50-0455 P10/10	Celanese Corporation	PP, Unspecified	Celstran®
Hifax CA45F	LyondellBasell Industries	TPO (POE)	Hifax
Kumho SBR 1712P	Korea Kumho Petrochemical Co., Ltd.	SBR, Emulsion	Kumho SBR