LNP™ LUBRICOMP™ RFL36XXY compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TTwqKW_LNP-LUBRICOMP-RFL36XXY-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RFL36XXY is a compound based on Nylon 66 containing 30% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RFL-4036 Product reorder name: RFL36XXY |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 1.1 | % | ASTM D955 |
| Across Flow : 24 hr | 1.2 | % | ISO 294-4 |
| Flow : 24 hr | 0.32 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.62 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11200 | MPa | ASTM D638 |
| -- | 9800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 139 | MPa | ASTM D638 |
| Break | 138 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.1 | % | ASTM D638 |
| Break | 2.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 9740 | MPa | ASTM D790 |
| -- 5 | 9700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 211 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 236 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.59 | ||
| vs. Itself - Static | 0.46 | ||
| Wear Factor - Washer | 12.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| -40°C 7 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 8 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 910 | J/m | ASTM D4812 |
| 23°C 9 | 51 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.0 | J | ASTM D3763 |
| -- | 2.89 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 249 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 248 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.8E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Softell DKG150N | LyondellBasell Industries | TPO (POE) | Softell |
| Borealis PP RB363 | Borealis AG | PP, Unspecified | Borealis PP |
| Enviramid® N2350HL BK | Ravago Manufacturing Americas, LLC | Nylon 6 | Enviramid® |
| Hapflex™ 871-4 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| Hostacom BB 1162 F M C13034 | LyondellBasell Industries | PP Copolymer | Hostacom |