CYROLITE® CG-97

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Cyro LLC
Trademark:	CYROLITE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	TTgaZB_CYROLITE-CG-97.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

CYROLITE CG-97 compound is an impact-modified acrylic-based multipolymer for molding and extrusion of medical applications.

Typical properties of CYROLITE® acrylic-based multipolymer compounds are:

excellent chemical resistance to fats and oils

excellent bonding and welding capabilities

excellent bonding to PVC tubing

good impact strength

good light transmission

good resistance to EtO, gamma and E-beam sterilization

The special properties of CYROLITE CG-97 compound are:

superior resistance to lipids

excellent gamma sterilization color stability

high impact resistance

very good resistance to alcohol

Used for injection molding and extrusion of medical devices.

General Information
Additive	Impact Modifier
Features	Alcohol Resistant Bondability E-beam Sterilizable Ethylene Oxide Sterilizable Good Chemical Resistance Good Color Stability High Clarity High Impact Resistance Impact Modified Radiation Sterilizable Weldable
Uses	Medical/Healthcare Applications
Agency Ratings	EC 1907/2006 (REACH) FDA 21 CFR 176.170
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.08	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (230°C/5.0 kg)	1.8	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.50 to 0.70	%	ASTM D955
Water Absorption (Saturation)	0.40	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (L-Scale)	47		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1860	MPa	ASTM D638
Tensile Strength	36.3	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	3.8	%
Break	14	%
Flexural Modulus	1860	MPa	ASTM D790
Flexural Strength	67.6	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 3.18 mm)	120	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm)	70.0	°C	ASTM D648
Vicat Softening Temperature	90.0	°C	ASTM D1525
CLTE - Flow (0 to 156°C)	9.5E-5	cm/cm/°C	ASTM D696

Optical	Nominal Value	Unit	Test Method
Transmittance (3200 µm)	87.0	%	ASTM D1003
Haze (81.3 µm)	5.0	%	ASTM D1003
Yellowness Index (3.20 mm)	-0.30	YI	ASTM D1925

Injection	Nominal Value	Unit
Drying Temperature	71.1	°C
Drying Time	3.0 to 4.0	hr
Processing (Melt) Temp	216 to 249	°C
Mold Temperature	48.9 to 82.2	°C

Resin Grade	Manufacturer	Category	Trademark
ReoFlex® 60	Smooth-On, Inc	PUR, Unspecified	ReoFlex®
Milastomer™ 5020BS	Mitsui Chemicals America, Inc.	TPV	Milastomer™
SEETEC EVA VE700	Lotte Chemical Corporation	EVA	SEETEC EVA
Witcom POM-C 4L3	Witcom Engineering Plastics B.V.	Acetal (POM) Copolymer	Witcom POM-C
ACCUTECH™ CP0437M30L	ACLO Compounders Inc.	PP Copolymer	ACCUTECH™