Vipel® K022-ACT-30
| Category: | Vinyl Ester , Vinyl Ester |
| Manufacturer: | AOC, L.L.C. |
| Trademark: | Vipel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TSf9mv_VipelK022ACT30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AOC's Vipel K022 series is a brominated bisphenol A epoxy vinyl ester resin dissolved in styrene. Vipel K022 series is ideally suited for use in hand lay-up, spray-up, filament winding and pultrusion processes where outstanding mechanical properties and excellent resistance to chemicals and heat are required. Vipel K022-CN series contains antimony products. BENEFITS Fire Retardant Some Vipel K022 versions do not require antimony trioxide to meet ASTM E 84 Class I flame spread requirements. Mechanical Properties Vipel K022 is suitable for moldings that are subjected to particularly high static or dynamic loads. Vinyl ester resins have excellent resistance to sustained heat. Versatile Wide formulating capabilities allow for use in many processes and for optimization of cost/performance. Corrosion Resistance Vipel K022 is highly resistant to a number of chemical environments. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Styrene Content | 40 | % |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Spread | 25.0 | ASTM E84 | |
| Smoke Developed | 500 | ASTM E84 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Gel to Peak | 14.0 | min | |
| Peak Exotherm | 177 | °C | |
| Thixotropic Index 1 | 2.50 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 39 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3590 | MPa | ASTM D638 |
| Tensile Strength | 86.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.7 | % | ASTM D638 |
| Flexural Modulus | 3650 | MPa | ASTM D790 |
| Flexural Strength | 147 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 116 | °C | ASTM D648 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density | 1.15 | g/cm³ | |
| Viscosity (25°C, Brookfield RVT) | 0.45 | Pa·s | |
| Gel Time (25°C) | 30 | min |
| Note Message | |
|---|---|
| 1 . | 2/20 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niche PA66GF43N | Niche Polymer, LLC | Nylon 66 | Niche |
| Hostacom TSOP EM5 G73024 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Karina CLEAR PVC COMPOUND 85/201-DA-IS-SI-AT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Wanthane® WHT-1198F | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| LNP™ LUBRICOMP™ KL004A compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |