Epoxies, Ect. 50-2366 FR
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Epoxies, Etc. |
| Trademark: | Epoxies, Ect. |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TSYzDX_Epoxies-Ect-50-2366-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
50-2366FR is a new thermally conductive polyurethane potting compound. This flexible system is designed for low stress on sensitive components during and after cure. 50-2366FR polyurethane resin system is formulated for applications requiring low exotherm, low shrinkage, and excellent electrical properties. This system is a good choice for potting applications containing surface mount components or any application requiring low stress, thermal conductivity and flame retardancy. 50-2366FR is suitable for outdoor use. For a very fast curing version of this product consider the 50-2370FR. This product will be tack free in 20 minutes. 50-2366FR is fungus resistant and passes Fungus Resistance Testing (MIL-STD-810F, Method 508.5). Features:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Molding Shrinkage - Flow | 0.50 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 1.6E-4 | cm/cm/°C | |
| Thermal Conductivity | 1.2 | W/m/K |
| Electrical | Nominal Value | Unit | |
|---|---|---|---|
| Surface Resistivity | 6.0E+17 | ohms |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Operating Temperature | -65.0 to 135 | °C | |
| Thermal Shock (-60 to 135°C) | Pass |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | Black | ||
| Mix Ratio by Weight (PBW) | |||
| Part A | 100 | ||
| Part B | 20 | ||
| Mix Ratio by Volume (PBV) | |||
| Part A | 100 | ||
| Part B | 26 | ||
| Density | |||
| 25°C 1 | 1.21 | g/cm³ | |
| 25°C 2 | 1.56 | g/cm³ | |
| Viscosity | |||
| -- 3 | 0.15 | Pa·s | |
| -- 4 | 17 | Pa·s | |
| Curing Time | |||
| 100°C | 0.33 to 0.50 | hr | |
| 60°C | 2.0 | hr | |
| 25°C | 24 | hr | |
| Shelf Life | 12 | month |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Water Absorption | |||
| -- 5 | 0.074 | % | |
| -- 6 | 0.18 | % | |
| Shore Hardness (Shore D) | 65 | ||
| Tensile Strength | 15.2 | MPa | |
| Tensile Elongation at Break | 35 | % | |
| Electric Strength | 21 | kV/mm | |
| Relative Permittivity (100 Hz) | 4.30 | ||
| Volume Resistivity | 2.1E+14 | ohms·cm |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | Part B |
| 4 . | Part A |
| 5 . | 24 hours immersion |
| 6 . | 7 days immersion |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Versaflex™ 9570-1 | PolyOne Corporation | TPE | Versaflex™ |
| Latamid 12 G/50 | LATI S.p.A. | Nylon 12 | Latamid |
| INELEC PA610CF10 | Infinity LTL Engineered Compounds | Nylon 610 | INELEC |
| Makroblend® EC5005 HT | Covestro - Polycarbonates | PC+PBT | Makroblend® |
| POCAN® KL 1-7265 POS151 901317 | LANXESS GmbH | PBT | POCAN® |