Greenflex® FD 50 F
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Greenflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TSYvF0_Greenflex-FD-50-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Greenflex FD 50 F is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. Films produced by Greenflex FD 50 F exhibit good optical and sealing properties, high flexibility and toughness. Main Application Greenflex FD 50 F is recommended for the production of agricultural films and water proofing membrane having outstanding mechanical performances (flexibility, elasticity and adherence) and dimensional stability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.40 | g/10 min | ISO 1133 |
| Vinyl Acetate Content | 17.0 | wt% | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, Injection Molded | 90 | ||
| Shore D, Injection Molded | 39 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 30 to 150 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : Blown Film | 55.0 | MPa | |
| 1% Secant, TD : Blown Film | 60.0 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, Blown Film | 4.50 | MPa | |
| TD : Yield, Blown Film | 4.00 | MPa | |
| MD : Break, Blown Film | 35.0 | MPa | |
| TD : Break, Blown Film | 30.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, Blown Film | 450 | % | |
| TD : Break, Blown Film | 700 | % | |
| Dart Drop Impact 1(Blown Film) | > 700 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD | 20.0 | kN/m | |
| TD | 44.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 67.0 | °C | ISO 306/A |
| Melting Temperature | 88.0 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, Blown Film) | 87 | ASTM D2457 | |
| Haze (Blown Film) | 1.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ CP0436W40L1 | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Clariant PP HF-HP | Clariant Corporation | PP, Unspecified | Clariant PP |
| Hytrel® G5544 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| LEXAN™ LGK4030 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| LNP™ STAT-KON™ OX00428 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ STAT-KON™ |