LNP™ THERMOCOMP™ SF006 compound
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TSVAGG_LNP-THERMOCOMP-SF006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* SF006 is a compound based on Nylon 12 resin containing 30% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound SF-1006 Product reorder name: SF006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 to 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.74 to 0.81 | % | ISO 294-4 |
| Flow : 24 hr | 0.21 to 0.30 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.14 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.22 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6550 | MPa | ASTM D638 |
| -- | 6590 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 107 | MPa | ASTM D638 |
| Break | 108 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 4.7 | % | ASTM D638 |
| Break | 4.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5860 | MPa | ASTM D790 |
| -- | 6240 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 171 | MPa | ASTM D790 |
| -- | 169 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256 |
| 23°C 2 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 950 | J/m | ASTM D4812 |
| 23°C 3 | 58 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 13.0 | J | ASTM D3763 |
| -- | 3.61 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 164 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 162 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.1E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 216 to 227 | °C | |
| Middle Temperature | 221 to 232 | °C | |
| Front Temperature | 227 to 238 | °C | |
| Processing (Melt) Temp | 227 to 238 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MOSTEN GB 002 | UNIPETROL RPA | PP Homopolymer | MOSTEN |
| Gallonprene® GP410-6003 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Karina NATURAL PVC COMPOUND 890-25/ 1-CR-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| KMI PA KM66-01MC | KMI Group, Inc. | Nylon 66 | KMI PA |
| Hostacom DYS 707N E G31463 | LyondellBasell Industries | PP Copolymer | Hostacom |