DuPure® L 50 E
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ducor Petrochemicals BV |
| Trademark: | DuPure® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TR1m00_DuPure-L-50-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description DuPure L 50 E is a polypropylene homopolymer for extrusion applications. DuPure L 50 E shows an easy processability and a good stiffness/impact balance at ambient temperature. Applications DuPure L 50 E is suitable for: cast films, OPP films, tape yarns, monofilaments, strapping, and thermoformed parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.5 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 77.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 9.0 | % | |
| Break | > 50 | % | |
| Coefficient of Friction (vs. Itself - Dynamic, Cast Film) | > 0.50 | DIN 53375 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation | DIN 53455 | ||
| MD : Break, Cast Film | 670 | % | |
| TD : Break, Cast Film | 700 | % | |
| Flexural Modulus | DIN 53121 | ||
| MD : Cast Film | 670 | MPa | |
| TD : Cast Film | 650 | MPa | |
| Dart Drop Impact 1(Cast Film) | 330 | g | ASTM D1709 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 1.6 | kJ/m² | |
| 23°C | 3.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 130 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 85.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ISO 306/A |
| -- | 90.0 | °C | ISO 306/B |
| Melting Temperature (DSC) | 163 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, Cast Film) | 130 | ISO 2813 | |
| Haze (Cast Film) | 0.50 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 2 | DIN 53455 | ||
| MD | 43.0 | MPa | |
| TD | 39.0 | MPa |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP320M | LyondellBasell Industries | PP Random Copolymer | Moplen |
| VYLOPET® EMC333 | TOYOBO America, Inc. | PC+PBT | VYLOPET® |
| EPO-TEK® H70E-4 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Sylvin 8240-80FU Grey 9570 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| OTECH TPO OTR9088 - Gasket | OTECH Corporation | TPE | OTECH TPO |