LNP™ THERMOCOMP™ Noryl_FM3020 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TQsG61_LNP-THERMOCOMP-Noryl-FM3020-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP NORYL_FM3020 compound is GR/MR 30%, high modulus structural foam. 10% weight reduction, 0.250" wall thickness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 1.19 | g/cm³ | |
| -- | 1.32 | g/cm³ | |
| Molding Shrinkage | Internal Method | ||
| Flow : 6.40 mm | 0.25 | % | |
| Across Flow : 3.20 mm | 0.30 | % | |
| Water Absorption (24 hr) | 0.080 | % | ASTM D570 |
| Foam - Physical 2 | 10 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Mechanical 3 | 10 | % | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Impact 4 | 10 | % | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Thermal 5 | 10 | % | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Electrical 6 | 20 | % | Internal Method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Foam - Flame Class Minimum Density | 1.120 | g/cm³ | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Weight Reduction | 10 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 83 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 6.35 mm) | 72.4 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 6.35 mm) | 2.0 | % | ASTM D638 |
| Flexural Modulus (6.40 mm) | 6550 | MPa | ASTM D790 |
| Flexural Strength (Yield, 6.40 mm) | 105 | MPa | ASTM D790 |
| Poisson's Ratio | 0.38 | ASTM D638 | |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Static | 0.54 | ||
| vs. Steel - Static | 0.51 | ||
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 100 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 118 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 110 | °C | |
| CLTE | ASTM E831 | ||
| Flow : -40 to 95°C | 2.3E-5 | cm/cm/°C | |
| Transverse : -40 to 95°C | 3.4E-5 | cm/cm/°C | |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Arc Resistance 7 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (2.90 mm) | V-1 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 240 to 260 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Foam molded |
| 2 . | 6.4 mm wt reduction |
| 3 . | 6.4 mm wt reduction |
| 4 . | 6.4 mm wt reduction |
| 5 . | 6.4 mm wt reduction |
| 6 . | 6.4 mm wt reduction |
| 7 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Primefin V515R34 | Lucent Polymers, Inc. | PP, Unspecified | Primefin |
| MEGOLON™ S501 | AlphaGary | TP, Unspecified | MEGOLON™ |
| SABIC® STAMAX 40YM243 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® STAMAX |
| NYCOA Polyamide 2137 | Nycoa (Nylon Corporation of America) | Nylon Copolymer | NYCOA Polyamide |
| EPLAMID 66 GFS 33 HS NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |