Alathon® M5350
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TQoo5n_Alathon-M5350.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Alathon M5350 is a copolymer with a narrow molecular weight distribution. This resin provides high impact strength, excellent color, low odor and good processing stability. Typical applications include open head pails, large shipping containers and 55-gallon drum lids. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.53 to 0.59 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| Spiral Flow | 20.6 | cm | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- | 1020 | MPa | |
| 1% Secant | 808 | MPa | |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 28.0 | MPa | |
| Break | > 29.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 9.0 | % | |
| Break | > 2000 | % | |
| Flexural Modulus 4 | ASTM D790 | ||
| -- | 1370 | MPa | |
| 1% Secant | 1290 | MPa | |
| 2% Secant | 1060 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 44 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 73.3 | °C | ASTM D648 |
| Brittleness Temperature | < -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 126 | °C | ASTM D1525 |
| Peak Melting Temperature | 131 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 116 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mold Max® 15T | Smooth-On, Inc | Silicone | Mold Max® |
| Sinvicomp SZF6208 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| ALCUDIA® EVA PA-460 | REPSOL | EVA | ALCUDIA® EVA |
| Monprene® CP-38134 XRD1 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| LNP™ STAT-KON™ WS002I compound | SABIC Innovative Plastics | PBT | LNP™ STAT-KON™ |