Clariant ABS ABS4500G10
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TOLUNl_Clariant-ABS-ABS4500G10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The Notched Izod Impact Strength was tested on a natural colored specimen. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 60 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 68.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 4480 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 104 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 98.9 | °C | ASTM D648 |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 204 - 249 | °C | |
| Middle Temperature | 204 - 249 | °C | |
| Front Temperature | 204 - 249 | °C | |
| Processing (Melt) Temp | 204 - 246 | °C | |
| Melt Temperature (Aim) | 227 | °C | |
| Mold Temperature | 23.9 - 79.4 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 - 2.07 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Cushion | 3.18 - 6.35 | mm |
| Injection instructions |
|---|
| The minimum injection pressure to achieve 95% fill of the part during the boost injection pressure phase should be used. The hold pressure should be between 30% and 75% of the initial injection pressure. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuman ABS SP791 | Shuman Plastics, Inc. | ABS | Shuman ABS |
| FLEXCHEM™ 6053 | Colorite Polymers | PVC, Flexible | FLEXCHEM™ |
| 3M™ Dyneon™ Fluoroelastomer MIP 8780 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| Sylvin 83041-84 Grey 9598 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ESTOPLAST XU 230HSNN01 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |