TECHNYL® A 218G V33 BLACK 34N
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TNvM0D_TECHNYL-A-218G-V33-BLACK-34N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® A 218G V33 Black 34N is a polyamide 66, reinforced with 33% of glass fiber, heat stabilized, for injection molding. The product is available in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.39 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.80 | -- | % | ASTM D570 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11500 | 7900 | MPa | ISO 527-2/1A |
| Tensile Strength | ||||
| Break | 195 | -- | MPa | ASTM D638 |
| Break | 200 | 140 | MPa | ISO 527-2/1A |
| Tensile Elongation | ||||
| Break | 3.0 | -- | % | ASTM D638 |
| Break | 3.4 | -- | % | ISO 527-2/1A |
| Flexural Modulus | ||||
| -- | 9500 | -- | MPa | ASTM D790 |
| -- | 9500 | 7000 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 295 | -- | MPa | ASTM D790 |
| -- | 13.0 | 20.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | 19 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 92 | 98 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| 23°C | 120 | -- | J/m | ASTM D256 |
| 23°C | 12 | -- | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 1.8 MPa, Unannealed | 255 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| CLTE - Transverse (23 to 85°C) | 2.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 6.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 5.0E+14 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 34 | 29 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.70 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.010 | 0.11 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 450 | 425 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Baydur® 661 IBS (30 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| Chansieh Phenolic J-185 | Chansieh Enterprises Co., LTD. | Phenolic | Chansieh Phenolic |
| Kepamid® 2300MRH | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| Karina WHITE PVC COMPOUND 800-10/61-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® PA6/6 GF20 TL10 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |