LNP™ THERMOCOMP™ DC006ER compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TNQ7L7_LNP-THERMOCOMP-DC006ER-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* DC006ER is a compound based on Polycarbonate resin containing 30% Carbon Fiber. Added features of this material include: Easy Molding, Mold Release, Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound DC-1006 EM MR Product reorder name: DC006ER |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.040 to 0.10 | % | ASTM D955 |
| Across Flow : 24 hr | 0.30 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.35 to 0.40 | % | ISO 294-4 |
| Flow : 24 hr | 0.040 to 0.13 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.14 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.21 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 19600 | MPa | ASTM D638 |
| -- | 16700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 151 | MPa | ASTM D638 |
| Break | 149 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.9 | % | ASTM D638 |
| Break | 1.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 14500 | MPa | ASTM D790 |
| -- | 16500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 221 | MPa | ASTM D790 |
| -- | 226 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 69 | J/m | ASTM D256 |
| 23°C 2 | 7.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 480 | J/m | ASTM D4812 |
| 23°C 3 | 32 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 9.60 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 144 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 140 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 2.8E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® B1920 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| Sarlink® TPE ME-1390N-01 | Teknor Apex Company | TPE | Sarlink® TPE |
| Vinnolit® S 3268 | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| Evermore PUR SS-143G | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| MARPOL® P1902 | Marco Polo International, Inc. | POP | MARPOL® |