Message
Amodel AS -1133 HS is 33% glass fiber reinforced heat stable polyphthalamide (PPA) resin. Even those molded parts with wall thickness greater than 0.125 inches (3mm) have excellent structural integrity. The main characteristics of the structural resin include high thermal deformation temperature, high flexural modulus, high tensile strength, excellent creep resistance and low moisture absorption. -black: AS-1145 HS BK 324 -natural color: AS-1145 HS NT

General Information
Filler / Reinforcement	Glass fiber reinforced material, 45% filler by weight
Additive	heat stabilizer
Features	Good dimensional stability Low hygroscopicity Rigid, good High strength Good creep resistance Good chemical resistance Heat resistance, high Thermal Stability
Uses	Lawn and Garden Equipment Power/other tools Valve/valve components Industrial components Industrial application Thick wall fittings (parts) Machine/mechanical parts Metal substitution Connector Parts under the hood of a car Automotive Electronics Application in Automobile Field Fuel line General Shell
RoHS Compliance	RoHS compliance
Appearance	Black Natural color
Forms	Particle
Processing Method	Injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.56	--	g/cm³	ISO 1183/A
Molding Shrinkage				ASTM D955
Flow	0.20	0.10	%	ASTM D955
Transverse flow	0.60	0.10	%	ASTM D955
Water Absorption (24 hr)	0.12	--	%	ASTM D570

Hardness	Dry	Conditioned	Unit	Test Method
Rockwell Hardness (R-Scale)	125	--		ASTM D785

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus
--	17200	17200	MPa	ASTM D638
--	16000	--	MPa	ISO 527-2
Tensile Strength
Fracture	259	228	MPa	ASTM D638
Fracture	263	--	MPa	ISO 527-2
Tensile Elongation
Fracture	2.6	2.1	%	ASTM D638
Fracture	2.7	--	%	ISO 527-2
Flexural Modulus
--	13800	13800	MPa	ASTM D790
--	14800	--	MPa	ISO 178
Flexural Stress
--	376	--	MPa	ISO 178
Yield	363	294	MPa	ASTM D790
Compressive Strength	314	302	MPa	ASTM D695
Shear Strength	108	91.7	MPa	ASTM D732
Poisson's Ratio	0.41	--		ASTM E132

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength	12	--	kJ/m²	ISO 179/1eA
Notched Izod Impact
--	120	100	J/m	ASTM D256
--	14	--	kJ/m²	ISO 180/1A
Unnotched Izod Impact	1300	--	J/m	ASTM D256

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, annealed, 3.18mm	301	--	°C	ASTM D648
1.8 MPa, not annealed	279	--	°C	ISO 75-2/A
1.8 MPa, annealed, 3.18mm	287	--	°C	ASTM D648
Continuous Use Temperature				ASTM D3045
-- ¹	165	--	°C	ASTM D3045
-- ²	185	--	°C	ASTM D3045
Melting Temperature	312	--	°C	ISO 11357-3, ASTM D3418
Linear thermal expansion coefficient				ASTM E831
Flow : 0 to 100°C	1.4E-5	--	cm/cm/°C	ASTM E831
Flow : 160 to 249°C	1.1E-5	--	cm/cm/°C	ASTM E831
Lateral : 0 to 100°C	5.0E-5	--	cm/cm/°C	ASTM E831
Lateral : 160 to 249°C	1.0E-4	--	cm/cm/°C	ASTM E831

Electrical	Dry	Conditioned	Unit	Test Method
Volume Resistivity	1.0E+16	2.0E+15	ohms·cm	ASTM D257
Dielectric Strength	22	22	kV/mm	ASTM D149
Dielectric Constant				ASTM D150
60 Hz	4.60	4.90		ASTM D150
1 MHz	4.40	4.50		ASTM D150
Dissipation Factor				ASTM D150
60 Hz	5.0E-3	9.0E-3		ASTM D150
1 MHz	0.016	0.021		ASTM D150
Arc Resistance	145	125	sec	ASTM D495
Comparative Tracking Index (CTI)	550	550	V	UL 746

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating ³(3.18 mm)	HB	--		UL 94

Injection	Dry	Unit
Drying Temperature	121	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.10	%
Hopper Temperature	79.4	°C
Rear Temperature	304 - 318	°C
Front Temperature	316 - 329	°C
Processing (Melt) Temp	321 - 343	°C
Mold Temperature	135	°C

Injection instructions
Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Injection instructions

Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Note Message
1 .	20000 hours
2 .	5000 hours
3 .	These flammability ratings do not represent the risk of these materials or any other materials in actual fire situations.

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	TNP9P7_Amodel-AS-1145-HS.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Telcar® TL-1431F	Teknor Apex Company	TPE	Telcar®
ESPOLEX 820	Sumitomo Chemical America, Inc.	TPO (POE)	ESPOLEX
Infino TK-6036H	SAMSUNG SDI CO., LTD.	PPA	Infino
LNP™ THERMOCOMP™ JF004P compound	SABIC Innovative Plastics	PESU	LNP™ THERMOCOMP™
POLYFLAM® RIPP 4000 E CS1	A. Schulman Europe	PP Copolymer	POLYFLAM®