KOPA® KN333G30HS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TNCHUZ_KOPA-KN333G30HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPA® KN333G30HS is a Polyamide 66 (Nylon 66) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.70 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 181 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 9.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 8630 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 284 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 250 | °C | |
| 1.8 MPa, Unannealed | 247 | °C | |
| Peak Melting Temperature | 255 | °C | ASTM D1525 |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150 | |
| Arc Resistance | 135 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP TIVAR® 88 Premium | Quadrant Engineering Plastic Products | UHMWPE | Quadrant EPP |
| RTP 1005 TFE 12 SI 2 | RTP Company | PBT | RTP |
| Vinnolit® EP 7060 | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| Nycast 6PA | Cast Nylons Ltd. | Nylon 6 | Nycast |
| Karina CLEAR PVC COMPOUND BTR-72/201-D-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |