SILICONE LUBRICATED POLYSTYRENE |
General Information | |
---|---|
Additive |
|
Features |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength (Break) | 24.8 | MPa | ASTM D638 |
Tensile Elongation (Break) | > 10 | % | ASTM D638 |
Flexural Modulus | 2340 | MPa | ASTM D790 |
Flexural Strength | 44.8 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact | 96 | J/m | ASTM D256 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 82.2 | °C | ASTM D648 |
Electrical | Nominal Value | Unit | Test Method |
---|---|---|---|
Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
Injection | Nominal Value | Unit | |
---|---|---|---|
Drying Temperature | 76.7 | °C | |
Drying Time | 2.0 to 4.0 | hr | |
Processing (Melt) Temp | 193 to 249 | °C | |
Mold Temperature | 37.8 to 65.6 | °C | |
Back Pressure | 0.345 to 0.689 | MPa | |
Screw Speed | 40 to 70 | rpm | |
Vent Depth | 0.013 to 0.025 | mm |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Radilon® S RCP3010LK 322 NER | Radici Plastics | Nylon 6 | Radilon® |
Trilliant™ HC HC5220-0040 RS Natural | PolyOne Corporation | PP, Unspecified | Trilliant™ HC |
INLUBE POMCCF30TF15 | Infinity LTL Engineered Compounds | Acetal (POM) Copolymer | INLUBE |
Osterlene® PPC-100-1.1 | Osterman & Company | PP Copolymer | Osterlene® |
Braskem PE HD7000C | Braskem | HDPE | Braskem PE |