LNP™ STAT-KON™ PD000 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TMbQaT_LNP-STAT-KON-PD000-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP STAT-KON PD000 is a compound based on PA 6 resin containing Carbon Powder. Added features include: Electrically Conductive. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 1.4 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 55.0 | MPa | |
| Break | 54.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 1.4 | % | |
| Break | 1.4 | % | |
| Flexural Modulus 1 | 3900 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 124 | MPa | |
| -- 4 | 125 | MPa | |
| Flexural Strain at Break 5 | 6.9 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 6(23°C) | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 7.3E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 8.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Break |
| 4 . | Yield |
| 5 . | 2 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trithene® TX 7003 | Petroquimica Triunfo | LDPE | Trithene® |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 6105 BR | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Axiall PVC 48451 NC | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Electrafil® HDPE C BK | Techmer Engineered Solutions | HDPE | Electrafil® |
| LinGen FR335 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TEEE | LinGen |