Braskem PP H 214
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Braskem |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TMGLb3_Braskem-PP-H-214.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: H 214 is a high melt flow rate homopolymer, with narrow molecular weight distribution, specially designed for fiber extrusion and nonwoven. This products presents excellent processability and produtivity, with good toughness/strain balance. Applications: Continuous filaments for high-tenacity yarns and spunbond nonwovens. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 26 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, Injection Molded | 101 | ASTM D785 | |
| R-Scale | 101 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 35.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Yield, Injection Molded) | 10 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus - 1% Secant | |||
| Injection Molded | 1300 | MPa | ASTM D790 |
| Injection Molded | 1500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, Injection Molded | 25 | J/m | ASTM D256 |
| 23°C, Injection Molded | 2.7 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, Injection Molded | 102 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 102 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, Injection Molded | 58.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 58.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 155 | °C | ISO 306/A, ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 901 TFE 10 Z | RTP Company | PSU | RTP |
| Vydyne® 47H BK0668 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| ALTECH® PA6 A 3230/500 GB15 GF15 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| LNP™ LUBRICOMP™ FL003 compound | SABIC Innovative Plastics | PE, Unspecified | LNP™ LUBRICOMP™ |
| PEXLOY™ PXP-413UV-NATURAL | Pier One Polymers, Inc. | PC+Polyester | PEXLOY™ |