Generic PPS
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TLoRRQ_Generic-PPS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPS This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.31 - 1.80 | g/cm³ | ASTM D792 |
| 23°C | 1.35 - 1.36 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (315°C/5.0 kg) | 75 - 200 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.030 - 1.4 | % | ASTM D955 |
| Transverse flow : 23°C | 0.43 - 1.5 | % | ASTM D955 |
| 23°C | 0.18 - 2.3 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.020 - 0.031 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 92 - 126 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2240 - 28000 | MPa | ASTM D638 |
| 23°C | 3390 - 15100 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 50.0 - 160 | MPa | ASTM D638 |
| Fracture, 23°C | 50.0 - 159 | MPa | ASTM D638 |
| Fracture, 23°C | 62.7 - 92.4 | MPa | ISO 527-2 |
| 23°C | 40.5 - 174 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 0.91 - 1.6 | % | ASTM D638 |
| Fracture, 23°C | 0.40 - 4.1 | % | ASTM D638 |
| Fracture, 23°C | 0.60 - 25 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2400 - 24400 | MPa | ASTM D790 |
| 23°C | 3600 - 4500 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 57.5 - 254 | MPa | ASTM D790 |
| 23°C | 64.3 - 152 | MPa | ISO 178 |
| Coefficient of Friction | 0.090 - 0.40 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.1 - 7.9 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 1.1 - 51 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 25 - 83 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 53 - 2000 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 277 - 281 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 101 - 267 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 95.0 - 270 | °C | ISO 75-2/A |
| Melting Temperature | 278 - 280 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | |||
| Flow | 1.3E-5 - 5.3E-5 | cm/cm/°C | ASTM D696 |
| Flow | 5.0E-6 - 6.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 5.1E-5 - 6.3E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.29 - 20 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 6.0 - 2.5E+15 | ohms | ASTM D257 |
| Volume Resistivity | |||
| 23°C | 10 - 2.5E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+11 - 2.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 16 - 18 | kV/mm | ASTM D149 |
| 23°C | 17 - 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant (23°C) | 3.00 - 3.05 | ASTM D150 | |
| Dissipation Factor | |||
| 23°C | 6.5E-4 - 5.0E-3 | ASTM D150 | |
| 23°C | 1.0E-3 - 2.1E-3 | IEC 60250 | |
| Arc Resistance | 118 - 125 | sec | ASTM D495 |
| Comparative Tracking Index | 100 - 151 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 163 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.015 - 0.020 | % | |
| Rear Temperature | 240 - 323 | °C | |
| Middle Temperature | 297 - 329 | °C | |
| Front Temperature | 307 - 323 | °C | |
| Nozzle Temperature | 305 - 325 | °C | |
| Processing (Melt) Temp | 313 - 335 | °C | |
| Mold Temperature | 144 - 158 | °C | |
| Injection Pressure | 60.0 - 114 | MPa | |
| Holding Pressure | 45.0 - 72.5 | MPa | |
| Back Pressure | 0.310 - 1.58 | MPa | |
| Screw Speed | 55 - 128 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPSThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QR Resin QR-4000-GF10 | QTR, Inc. | PPE+PS+Nylon | QR Resin |
| Sinvicomp DBS3607 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| BJB Polyurethane WC-575 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Lifolit® E 60.1451/1 Glow i. t. Dark 6024 | Müller Kunststoffe GmbH | PVC, Flexible | Lifolit® |
| KEBAFLEX® SG 75 A.1 black | BARLOG plastics GmbH | TES | KEBAFLEX® |