LNP™ KONDUIT™ OX11315 compound
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ KONDUIT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TLhvga_LNPKONDUITOX11315compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* KONDUIT* OX11315 is a thermally conductive, electrically insulative, mineral filled PPS Flame Retardant compound. Also known as: LNP* KONDUIT* Compound OX11315 Product reorder name: OX11315 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.78 | g/cm³ | ASTM D792 |
| -- | 1.76 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.34 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.44 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.010 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | < 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 30100 | MPa | ASTM D638 |
| -- | 18400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 41.0 | MPa | ASTM D638 |
| Fracture | 54.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 0.20 | % | ASTM D638 |
| Fracture | 0.30 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 26500 | MPa | ASTM D790 |
| -- 5 | 21400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 84.0 | MPa | ISO 178 |
| Fracture, 50.0mm span 6 | 82.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 16 | J/m | ASTM D256 |
| 23°C 7 | 1.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 54 | J/m | ASTM D4812 |
| 23°C 8 | 3.9 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 5.14 | J | ASTM D3763 |
| -- | 1.14 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 275 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 9 | 275 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 242 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 10 | 238 | °C | ISO 75-2/Af |
| Specific Heat | 1260 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | ASTM E1461 | ||
| -- 11 | 3.5 | W/m/K | ASTM E1461 |
| -- 12 | 15 | W/m/K | ASTM E1461 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.4E+15 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-0 | UL 94 | |
| 2.50 mm | 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Shot Size | 50 - 75 | % | |
| Rear Temperature | 316 - 343 | °C | |
| Middle Temperature | 316 - 343 | °C | |
| Front Temperature | 316 - 343 | °C | |
| Processing (Melt) Temp | 321 - 349 | °C | |
| Mold Temperature | 110 - 150 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| 11 . | through-plane, 10*10*3mm sample |
| 12 . | in-plane, ø25*0.4mm disc |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID庐 6 BT TLS | Plastcom | Nylon 6 | SLOVAMID® 6 |
| NYCOA Polyamide 2276 | Nycoa (Nylon Corporation of America) | Nylon Copolymer | NYCOA Polyamide |
| Alathon® M6010SB | LyondellBasell Industries | HDPE, MMW | Alathon® |
| Axiall PVC 19802 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Hostacom EKC 330N E1 D62813 | LyondellBasell Industries | PP Copolymer | Hostacom |