Product Profile:
PLEXIGLAS® Resist zk6HF is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).

Typical properties of impact-modified PLEXIGLAS® molding compounds are

high weather resistance

excellent transmission and clarity

brilliant appearance

the pleasant feel and sound of the moldings.

PLEXIGLAS® Resist zk6HF is characterized by the following special properties:

excellent break resistance and impact strength

improved resistance to stress cracking

very good flow.

Application:
Used for injection molding as well as for extruding sheets and profiles.

Examples:
applications involving thin walls and long flow paths, thin-walled components; items requiring accurate mold surface reproduction, such as very finely textured luminaire covers.

General Information
Additive	Impact Modifier
Features	Amorphous Good Flow Good Weather Resistance High Clarity High ESCR (Stress Crack Resist.) High Impact Resistance Pleasing Surface Appearance Soft
Uses	Lighting Diffusers Profiles Sheet Thin-walled Parts
Forms	Pellets
Processing Method	Electrostatic Spray Coating Extrusion Injection Molding Profile Extrusion Sheet Extrusion
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density	1.16	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	4.20	cm³/10min	ISO 1133
Water Absorption			ISO 62
23°C, 24 hr	1.8	%
Equilibrium, 23°C, 50% RH	0.50	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1900	MPa	ISO 527-2/1
Tensile Stress (Yield)	45.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	5.0	%	ISO 527-2/50
Nominal Tensile Strain at Break	50	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	75	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	94.0	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	1.1E-4	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94
Fire Rating	B2		DIN 4102

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.490		ISO 489
Transmittance ¹	91.0	%	ISO 13468-2

Injection	Nominal Value	Unit
Drying Temperature	> 80.0	°C
Drying Time	2.0 to 3.0	hr
Processing (Melt) Temp	220 to 260	°C
Mold Temperature	50.0 to 70.0	°C

Note Message
1 .	D65

Resin Grade	Manufacturer	Category	Trademark
POLYPRO® 5014L	YUHWA Korea Petrochemical Ind. Co., Ltd.	PP Homopolymer	POLYPRO®
SUMILITE® PVC VSL-4610-N	Sumitomo Bakelite Co., Ltd.	PVDC	SUMILITE® PVC
VITAMIDE® AX10NT6264	Jackdaw Polymers	Nylon 66	VITAMIDE®
CP PRYME® Polypropylene PPH100-20M	Chase Plastics Services Inc.	PP Homopolymer	CP PRYME® Polypropylene
Latamid 66 E21 G/15	LATI S.p.A.	Nylon 66	Latamid