INEOS PP H13M-00
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TKLZ2K_INEOS-PP-H13M-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| H13M-00 is a medium-term heat aging polypropylene homopolymer designed for injection molding applications such as automotive parts, appliances and medical and rigid packaging. This grade benefits from a good retention of physical properties when exposed to higher in-service temperatures over an extended period of time, even following hot-water extraction. This material has been recognized by UL for sustained use at 100°C and meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.911 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 37.0 | MPa | |
| Break | 17.1 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 9.1 | % | |
| Break | 140 | % | |
| Flexural Modulus - 1% Secant | 1650 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 32 | J/m | ASTM D256 |
| Notched Izod Impact (Area) (23°C) | 3.10 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 105 | °C | ASTM D648 |
| RTI Elec (6.00 mm) | 100 | °C | UL 746 |
| RTI Imp (6.00 mm) | 100 | °C | UL 746 |
| RTI Str (6.00 mm) | 100 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (6.00 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°) | 92 | ASTM D2457 | |
| Haze 3(1270 µm) | 76 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3677 TRN700 UV AF | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Tenac™-C GN755 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| PLUSTEK PB302G50BK39P | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| Sylvin 83054-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8940-65 BLACK | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |