Thermx® CGT33
| Category: | PCT , Polycyclohexylenedimethylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Thermx® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TKHeUQ_Thermx-CGT33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermx® CGT33 is a 30% glass fiber reinforced and toughened polycyclohexylenedimethylene terephthalate for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.30 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.4 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 110 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.8 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 7600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength (23°C) | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | °C | ISO 75-2/A |
| Melting Temperature 1 | 285 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 4.8E-5 | cm/cm/°C | |
| Transverse | 9.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength | 35 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Processing (Melt) Temp | 295 to 310 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TP SD 310 90A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| Sinvicomp DBS8615 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| DJSilicone NE-7130 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| EPLAMID 66 MOS2 %2 GFR 40 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| IPC PP 4830H-MLGF8-R2-UV | International Polymers Corporation | PP, Unspecified | IPC PP |