HAIPLEN EP70 C5
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TK93gP_HAIPLEN-EP70-C5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HAIPLEN EP70 C5 is a polypropylene copolymer (PP Copoly) product, which contains 25% calcium carbonate filler. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.1 | % | ASTM D955 |
| Transverse flow | 1.1 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 22.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 20 | % | ASTM D638, ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 50 | kJ/m² | ISO 179 |
| Notched Izod Impact | 45 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 115 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ASTM D1525, ISO 306/A50 1 1 |
| -- | 80.0 | °C | ASTM D1525, ISO 306/B50 2 2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 | |
| Oxygen Index | 21 | % | ASTM D2863 |
| Additional Information |
|---|
| Granule Humidity, TARO 002: 0.05%Density, ISO 118: 1.07 to 1.09 Mg/m³Density. ASTM D792: 1.07 to 1.09 Mg/m³Notched Izod Impact Strength , ISO 180, 23°C: 45 J/mCharpy Impact Strength, ASTM D256: 50 kJ/m²CTI IEC 112, IEC 60112, Method A: >600 V |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 190 - 220 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 速率 A (50°C/h), 压 力1 (10N) |
| 2 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resirene 6420 | Resirene, S.A. de C.V. | PS (HIPS) | Resirene |
| BMC 501E | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| GELAST GT75IT | Guang Sung Plastics (GSPL) | TP, Unspecified | GELAST |
| Hostaform® C 9021 10/9005 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Iupilon® EGN2020KR | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |