Prixene® PH060I04
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | POLYMAT |
| Trademark: | Prixene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TIq2m9_Prixene-PH060I04.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Prixene® PH060I04 is a resin of polypropylene homopolymer of low fluidity index, with normal distribution of molecular weights and additives for general use. Resin applications are in compounds, film and injection. The feature presented is good stability in the process. The product form is in pellets. PP for injection molding and extrusion. The material complies with FDA regulation title 21.CFR177.1520 (.C) 2.1 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 35.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 12 | % | ASTM D638 |
| Flexural Modulus | 1520 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 27 | J/m | ASTM D256 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SCR7F-7015A | Spartech Polycom | PC | Spartech |
| Colorite Rigid PVC 2201 | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| Hoffman PVC V0-072x1 CLEAR | Hoffman Plastic Compounds Inc. | PVC, Flexible | Hoffman PVC |
| Sylvin 8240-80FUV White 1513 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| API II 395 | API II, Inc. | PS (GPPS) | API II |