LNP™ LUBRICOMP™ DL002ER compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TIXXtO_LNP-LUBRICOMP-DL002ER-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DL002ER is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Wear Resistant, Easy Molding, Mold Release. Also known as: LNP* LUBRICOMP* Compound DL-4020 EM MR Product reorder name: DL002ER |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.60 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 to 0.90 | % | ASTM D955 |
| Across Flow : 24 hr | 0.79 | % | ISO 294-4 |
| Flow : 24 hr | 0.70 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 55.8 | MPa | ASTM D638 |
| Yield | 56.0 | MPa | ISO 527-2 |
| Break | 49.0 | MPa | ASTM D638 |
| Break | 46.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.9 | % | ASTM D638 |
| Yield | 5.8 | % | ISO 527-2 |
| Break | 66 | % | ASTM D638 |
| Break | 71 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 2200 | MPa | ISO 178 |
| Flexural Stress | 73.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.24 | ||
| vs. Itself - Static | 0.075 | ||
| Wear Factor - Washer | 34.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 2 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2500 | J/m | ASTM D4812 |
| 23°C 3 | 170 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 40.2 | J | ASTM D3763 |
| -- | 44.3 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 135 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 135 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 124 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 125 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.2E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 304 to 316 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 299 to 316 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier PH350 | Premier Polymers, LLC. | PP Homopolymer | Premier |
| Telcar® GS4002 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| ANYPOL SE-3000 | SH Energy & Chemical | PS (EPS) | ANYPOL |
| HiFill® PA4/6 GF30 FR HS L | Techmer Engineered Solutions | Nylon 46 | HiFill® |
| INSULCAST® RTVS Primer 41 | ITW Polymers Coatings North America | Silicone | INSULCAST® RTVS |